Date
WELDER PERFORMANCE QUALIFIQATION RECORD ACCORDING TO ASME IX-2010,Add.2011
January 31, 2013
WPQ No.
MEW-S001
Revision
0
Suman Thalukder Delip S001 WPS-ME-001
Name: Stamp no. : WPS no.:
TESTING CONDITIONS AND QUALIFICATION LIMITS
Welding variables (QW-350)
Actual values
Range of qualification
SMAW Manual NA NA
SMAW Manual NA NA
P No. 1(SA 516 Gr.485)
P No. 1 through P No. 15F, P No. 34, and P No. 41 through P No. 49
Process Type Transfer mode GTAW Current/polarity Base metal P No (material specification) (QW-423)
SFA 5.1 E 7018 4 None NA 10 mm
Filler metal Specification (SFA) Filler metal Classification F-No.
(QW-433)
Backing (metal, weld metal, double welded) Filler type (Solid, metal cored or fluxcored) (GTAW/PAW) Deposit weld metal thickness (t)
(QW-451.1)
F no 4 without Backing
NA 20 plate & pipe dia > 24" (610 mm) O.D
2G
Position (QW-461.9)
pipe dia ≤ 24" (610 mm) O.D
F,H
fillet (plate & pipe)
F, H
≥ 73 mm outside dia.
NA NA NA NA NA
Pipe outside diameter Welding progression Consumable insert Gas/Flux type Inert gas backing
F, H
NA NA NA NA
VISUAL INSPECTION (QW-302.4) Acceptable
YES
NO
GUIDED BEND TEST RESULTS (QW-462) Sample
Type
Result
Inspeted By
Abel Vaz
1
SIDE
ACC
Organization
Lonester Alpha Laboratories
2
SIDE
ACC
Date
27 janurary 2013
FILLET TEST RESULTS (QW-180)
NA
Fracture test
Mactoetch (QW-184)
Fillet size
Concavity/Convexity
Inspected by
Organization
Report No.
Date VOLUMETRIC NDE (QW-191)
Film identification no.
Result
Remarks
NA
Film identification no.
Inspected by
Report number
Organization
Date
Result
Remarks
We, the undersigned, certify that the statements in this record are correct and that the test welds were prepared, welded and tested in accordance with the requirements of ASME IX-2010,Add.2011 Prepared by
Mohamed Ibrahim
Mostafa Farid
Reviewed by
Signature
Signature
Date
Date
WELDER PERFORMANCE QUALIFIQATION RECORD
Date
January 31, 2013
Date
WELDER PERFORMANCE QUALIFIQATION RECORD ACCORDING TO ASME IX-2010,Add.2011
January 31, 2013
WPQ No.
MEW-S002
Revision
0
Dolan Kanti Chowdhuri S002 WPS-ME-002
Name: Stamp no. : WPS no.:
TESTING CONDITIONS AND QUALIFICATION LIMITS
Welding variables (QW-350)
Actual values
Range of qualification
SMAW Manual NA NA
SMAW Manual NA NA
P No. 1(SA 516 Gr.485)
P No. 1 through P No. 15F, P No. 34, and P No. 41 through P No. 49
Process Type Transfer mode GTAW Current/polarity Base metal P No (material specification) (QW-423)
SFA 5.1 E 7018 4 Double Welded NA 10 mm
Filler metal Specification (SFA) Filler metal Classification F-No.
(QW-433)
Backing (metal, weld metal, double welded) Filler type (Solid, metal cored or fluxcored) (GTAW/PAW) Deposit weld metal thickness (t)
(QW-451.1)
F no 4 with/without Backing
NA 20 plate & pipe dia > 24" (610 mm) O.D
2G
Position (QW-461.9)
F,H
fillet (plate & pipe)
F, H
≥ 73 mm outside dia.
NA NA NA NA NA
Pipe outside diameter Welding progression Consumable insert Gas/Flux type Inert gas backing
F, H
pipe dia ≤ 24" (610 mm) O.D
NA NA NA NA
VISUAL INSPECTION (QW-302.4) Acceptable
YES
NO
GUIDED BEND TEST RESULTS (QW-462) Sample
Type
Result
Inspeted By
Abel Vaz
1
SIDE
ACC
Organization
Lonester Alpha Laboratories
2
SIDE
ACC
Date
27 janurary 2013
FILLET TEST RESULTS (QW-180)
NA
Fracture test
Mactoetch (QW-184)
Fillet size
Concavity/Convexity
Inspected by
Organization
Report No.
Date VOLUMETRIC NDE (QW-191)
Film identification no.
Result
Remarks
NA
Film identification no.
Inspected by
Report number
Organization
Date
Result
Remarks
We, the undersigned, certify that the statements in this record are correct and that the test welds were prepared, welded and tested in accordance with the requirements of ASME IX-2010,Add.2011 Prepared by
Mohamed Ibrahim
Mostafa Farid
Reviewed by
Signature
Signature
Date
Date
WELDER PERFORMANCE QUALIFIQATION RECORD
Date WPQ No.
January 31, 2013 MEW-S003
WELDER PERFORMANCE QUALIFIQATION RECORD
WPQ No.
MEW-S003
ACCORDING TO ASME IX-2010,Add.2011
Revision
0
Abdul Kader S003 WPS-ME-001
Name: Stamp no. : WPS no.:
TESTING CONDITIONS AND QUALIFICATION LIMITS
Welding variables (QW-350) Process Type Transfer mode GTAW Current/polarity Base metal P No (material specification) (QW-423)
Filler metal Classification (QW-433)
Backing (metal, weld metal, double welded) Filler type (Solid, metal cored or fluxcored) (GTAW/PAW) Deposit weld metal thickness (t)
Range of qualification
SMAW Manual NA NA
SMAW Manual NA NA
P No. 1(SA 516 Gr.485)
P No. 1 through P No. 15F, P No. 34, and P No. 41 through P No. 49
SFA 5.1 E 7018 4 Single Side Weld NA 10 mm
Filler metal Specification (SFA) F-No.
Actual values
(QW-451.1)
F no 4 without Backing
NA 20 plate & pipe dia > 24" (610 mm) O.D
2G
Position (QW-461.9)
pipe dia ≤ 24" (610 mm) O.D
F,H
fillet (plate & pipe)
F, H
≥ 73 mm outside dia.
NA NA NA NA NA
Pipe outside diameter Welding progression Consumable insert Gas/Flux type Inert gas backing
F, H
NA NA NA NA
VISUAL INSPECTION (QW-302.4) Acceptable
YES
NO
GUIDED BEND TEST RESULTS (QW-462) NA Sample
Type
Result
Inspeted By
1
SIDE
ACC
Organization
2
SIDE
ACC
Date
FILLET TEST RESULTS (QW-180)
NA
Fracture test
Mactoetch (QW-184)
Fillet size
Concavity/Convexity
Inspected by
Organization
Report No.
Date VOLUMETRIC NDE (QW-191)
Film identification no.
Result
Remarks
Film identification no.
Result
Remarks
PQR/ME/Kader
ACC.
Acc.Pores.
Inspected by
Report number
RT01
Organization
Date
1/22/2013
We, the undersigned, certify that the statements in this record are correct and that the test welds were prepared, welded and tested in accordance with the requirements of ASME IX-2010,Add.2011 Prepared by
Mohamed Ibrahim
Reviewed by
Signature
Signature
Date
Date
Mostafa Farid
WELDER PERFORMANCE QUALIFIQATION RECORD
Date
10-2-2013
WPQ No.
G 001
ACCORDING TO ASME IX-2010,Add.2011 Revision
0
Zulfiqar Ali G001
Name: Stamp no. :
TESTING CONDITIONS AND QUALIFICATION LIMITS
Welding variables (QW-350)
Actual values
Range of Qualified
GTAW Manual NA DCEN
GTAW Manual NA DCEN
P No. 1 to P No.1 (SA 106 Gr. B)
P No. 1 through P No. 15F, P No. 34, and P No. 41 through P No. 49
SFA 5.18 ER 70S-6 6 Without Backing Solid 8.74 mm NO
____ ____ F No 6 with/without Backing Solid max. 17mm ____
Process Type Transfer mode GTAW Current/polarity Base metal P No (material specification) (QW-423) Filler metal Specification (SFA) Filler metal Classification F-No. (QW-433) Backing (metal, weld metal, double welded) Filler type (Solid, metal cored or flux cored) (GTAW/PAW) Deposit weld metal thickness (t) (QW-451.1) Three Layers Minimum
YES
plate & pipe dia > 24" (610 mm) O.D
2G
Position (QW-461.9) Pipe outside diameter Welding progression Consumable insert Gas/Flux type Inert gas backing
2 inch NA NA SG-A Argon 99.997% (single) None VISUAL INSPECTION (QW-302.4) YES NO
(QW-452.3)
Acceptable
F, H
pipe dia ≤ 24" (610 mm) O.D
F,H
fillet (plate & pipe)
F, H
1 inch (25 mm) and over NA NA SG-A Argon 99.997% None
GUIDED BEND TEST RESULTS (QW-462) Sample 1 2
Type Transverse Face Bend Transverse Root Bend
NA NA Inspected by Organization
Welding Supervised by :
Company Report No. Date Conducted by
Lonestar Alpha Laboratories LMM/ 1300146 9-Feb-13 GMY
FILLET TEST RESULTS (QW-180) NA NA Mactoetch (QW-184) NA Concavity/Convexity NA Organization NA Report No.
Fracture test Fillet size Inspected by Report No.
Film identification no.
Result Accepted Accepted
Result NA
VOLUMETRIC NDE (QW-191) NA Remarks Film identification no. NA NA
NA
NA
NA Report number Date
NA NA NA NA
Result NA
Remarks NA
NA
NA
Mostafa M. Farid
We, the undersigned, certify that the statements in this record are correct and that the test welds were prepared, welded and tested in accordance with the requirements of ASME IX2010,Add.2011. Manufacturer: Metal Engineering Oil and Gas Division
Prepared by Signature Date
Reviewed by Signature Date