CHAPTER 14 POLYMER STRUCTURES PROBLEM SOLUTIONS
Hydrocarbon Molecules Polymer Molecules The Chemistry of Polymer Molecules
14.1
On the basis of the structures presented in this chapter, chapter, sketch repeat unit structures for for the following polymers: (a) polychlorotrifluoroethylene, and (b) poly(vinyl alcohol). Solution The repeat unit structures called for are sketched below.
(a) Polychlorotrifluoroethylene
(b) Poly(vinyl alcohol)
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Molecular Weight
14.2 Compute repeat unit molecular weights for the following: (a) poly(vinyl chloride), (b) poly(ethylene terephthalate), (c) polycarbonate, and (d) polydimethylsiloxane. Solution (a) For poly(vinyl chloride), each repeat unit consists of two carbons, three hydrogens, and one chlorine (Table 14.3).
If AC, AH and ACl represent the atomic weights of carbon, hydrogen, and
chlorine, respectively, then
m = 2( A AC) + 3( A AH) + ( A ACl)
= (2)(12.01 g/mol) + (3)(1.008 g/mol) + 35.45 g/mol = 62.49 g/mol
(b)
For poly(ethylene terephthalate), terephthalate), from Table 14.3, each repeat unit has ten carbons, eight
hydrogens, and four oxygens. Thus,
m = 10( A AC) + 8( AH) + 4( AO)
= (10)(12.01 g/mol) + (8)(1.008 g/mol) + (4)(16.00 g/mol) = 192.16 g/mol
(c) For polycarbonate, from Table 14.3, each repeat unit has sixteen carbons, carbons, fourteen hydrogens, and three oxygens. Thus,
m = 16( A AC) + 14( AH) + 3( AO)
= (16)(12.01 g/mol) + (14)(1.008 g/mol) + (3)(16.00 g/mol)
= 254.27 g/mol
(d) For polydimethylsiloxane, from Table 14.5, each repeat unit has two carbons, six hydrogens, one silicon and one oxygen. Thus,
m = 2( A AC) + 6( A AH) + ( A ASi) + ( A AO)
= (2)(12.01 g/mol) + (6)(1.008 g/mol) + (28.09 g/mol) + (16.00 g/mol) = 74.16 g/mol
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Molecular Weight
14.2 Compute repeat unit molecular weights for the following: (a) poly(vinyl chloride), (b) poly(ethylene terephthalate), (c) polycarbonate, and (d) polydimethylsiloxane. Solution (a) For poly(vinyl chloride), each repeat unit consists of two carbons, three hydrogens, and one chlorine (Table 14.3).
If AC, AH and ACl represent the atomic weights of carbon, hydrogen, and
chlorine, respectively, then
m = 2( A AC) + 3( A AH) + ( A ACl)
= (2)(12.01 g/mol) + (3)(1.008 g/mol) + 35.45 g/mol = 62.49 g/mol
(b)
For poly(ethylene terephthalate), terephthalate), from Table 14.3, each repeat unit has ten carbons, eight
hydrogens, and four oxygens. Thus,
m = 10( A AC) + 8( AH) + 4( AO)
= (10)(12.01 g/mol) + (8)(1.008 g/mol) + (4)(16.00 g/mol) = 192.16 g/mol
(c) For polycarbonate, from Table 14.3, each repeat unit has sixteen carbons, carbons, fourteen hydrogens, and three oxygens. Thus,
m = 16( A AC) + 14( AH) + 3( AO)
= (16)(12.01 g/mol) + (14)(1.008 g/mol) + (3)(16.00 g/mol)
= 254.27 g/mol
(d) For polydimethylsiloxane, from Table 14.5, each repeat unit has two carbons, six hydrogens, one silicon and one oxygen. Thus,
m = 2( A AC) + 6( A AH) + ( A ASi) + ( A AO)
= (2)(12.01 g/mol) + (6)(1.008 g/mol) + (28.09 g/mol) + (16.00 g/mol) = 74.16 g/mol
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.3
The number-average number-average molecular weight of a polypropylene is 1,000,000 g/mol. Compute Compute the degree of polymerization. Solution We are asked to compute the degree of polymerization for polypropylene, given that the
number-average molecular weight is 1,000,000 g/mol.
The repeat unit molecular molecular weight of
polypropylene is just
m = 3( A AC) + 6( AH)
= (3)(12.01 g/mol) + (6)(1.008 g/mol) = 42.08 g/mol
Now it is possible to compute the degree of polymerization using Equation 14.6 as
DP =
M n m
=
1,000,000 g/mol 42.08 g/mol
= 23,760 23,760
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.4
(a) Compute the repeat unit molecular weight of polystyrene. (b) Compute the number-average molecular weight for a polystyrene for which the degree of polymerization is 26,000. Solution
(a) The repeat unit molecular weight of polystyrene is called for in this portion of the problem. For polystyrene, from Table 14.3, each repeat unit has eight carbons and eight hydrogens. Thus,
m = 8( AC) + 8( AH)
= (8)(12.01 g/mol) + (8)(1.008 g/mol) = 104.14 g/mol
(b)
We are now asked to compute the number-average molecular weight. Since the degree of
polymerization is 26,000, using Equation 14.6 M n = ( DP )m = (26,000)(104.14 g/mol) = 2.70 × 10 6 g/mol
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.5
The following table lists molecular weight data for a polypropylene material. Compute (a) the number-average molecular weight, (b) the weight-average molecular weight, and (c) the degree of polymerization.
Molecular Weight Range (g/mol)
x i
wi
8,000–16,000
0.05
0.02
16,000–24,000
0.16
0.10
24,000–32,000
0.24
0.20
32,000–40,000
0.28
0.30
40,000–48,000
0.20
0.27
48,000–56,000
0.07
0.11
Solution (a) From the tabulated data, we are asked to compute
, the number-average molecular weight.
n
This is carried out below. Molecular wt Range
Mean M i
xi
x M i i
8,000–16,000
12,000
0.05
600
16,000–24,000
20,000
0.16
3200
24,000–32,000
28,000
0.24
6720
32,000–40,000
36,000
0.28
10,080
40,000–48,000
44,000
0.20
8800
48,000–56,000
52,000
0.07
3640
M n =
(b) From the tabulated data, we are asked to compute Molecular wt. Range
w
∑ x M = 33, 040 g/mol i
i
, the weight-average molecular weight.
Mean M i
wi
w M i i
8,000–16,000
12,000
0.02
240
16,000–24,000
20,000
0.10
2000
24,000–32,000
28,000
0.20
5600
32,000–40,000
36,000
0.30
10,800
40,000–48,000
44,000
0.27
11,880
48,000–56,000
52,000
0.11
5720
M w =
∑ w M = 36,240 g/mol i
i
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
(c) Now we are asked to compute the degree of polymerization, which is possible using Equation 14.6. For polypropylene, the repeat unit molecular weight is just
m = 3( AC) + 6( AH)
= (3)(12.01 g/mol) + (6)(1.008 g/mol) = 42.08 g/mol
And DP =
M n m
=
33,040 g/mol 42.08 g/mol
= 785
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.6
Molecular weight data for some polymer are tabulated here. Compute (a) the number-average molecular weight, and (b) the weight-average molecular weight. (c) If it is known that this material's degree of polymerization is 750, which one of the polymers listed in Table 14.3 is this polymer? Why? Molecular Weight Range g/mol 15,000–30,000
xi 0.04
wi 0.01
30,000–45,000
0.07
0.04
45,000–60,000
0.16
0.11
60,000–75,000
0.26
0.24
75,000–90,000
0.24
0.27
90,000–105,000
0.12
0.16
105,000–120,000
0.08
0.12
120,000–135,000
0.03
0.05
Solution (a) From the tabulated data, we are asked to compute
n
, the number-average molecular weight.
This is carried out below. Molecular wt. Range
Mean M i
xi
x M i i
15,000–30,000
22,500
0.04
900
30,000–45,000
37,500
0.07
2625
45,000–60,000
52,500
0.16
8400
60,000–75,000
67,500
0.26
17,550
75,000–90,000
82,500
0.24
19,800
90,000–105,000
97,500
0.12
11,700
105,000–120,000
112,500
0.08
9000
120,000–135,000
127,500
0.03
3825
M n =
∑ x M = 73,800 g/mol i
i
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
(b) From the tabulated data, we are asked to compute
w
, the weight-average molecular weight.
This determination is performed as follows: Molecular wt. Range
Mean M i
wi
w M i i
15,000–30,000
22,500
0.01
225
30,000–45,000
37,500
0.04
1500
45,000–60,000
52,500
0.11
5775
60,000–75,000
67,500
0.24
16,200
75,000–90,000
82,500
0.27
22,275
90,000–105,000
97,500
0.16
15,600
105,000–120,000
112,500
0.12
13,500
120,000–135,000
127,500
0.05
6375
M w =
∑ w M = 81,450 g/mol i
i
(c) We are now asked if the degree of polymerization is 750, which of the polymers in Table 14.3 is this material? It is necessary to compute m in Equation 14.6 as
m=
M n DP
=
73,800g/mol 750
= 98.4g/mol
The repeat unit molecular weights of the polymers listed in Table 14.3 are as follows:
Polyethylene—28.05 g/mol Poly(vinyl chloride)—62.49 g/mol Polytetrafluoroethylene—100.02 g/mol Polypropylene—42.08 g/mol Polystyrene—104.14 g/mol Poly(methyl methacrylate)—100.11 g/mol Phenol-formaldehyde—133.16 g/mol Nylon 6,6—226.32 g/mol PET—192.16 g/mol Polycarbonate—254.27 g/mol Therefore, polytetrafluoroethylene is the material since its repeat unit molecular weight is closest to that calculated above.
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.7
Is it possible to have a poly(methyl methacrylate) homopolymer with the following molecular weight data and a of polymerization of 530? Why or why not? Molecular Weight Range (g/mol) 8,000–20,000
wi 0.02
x i 0.05
20,000–32,000
0.08
0.15
32,000–44,000
0.17
0.21
44,000–56,000
0.29
0.28
56,000–68,000
0.23
0.18
68,000–80,000
0.16
0.10
80,000–92,000
0.05
0.03
Solution This problem asks if it is possible to have a poly(methyl methacrylate) homopolymer with the given molecular weight data and a degree of polymerization of 530. The appropriate data are given below along with a computation of the number-average molecular weight.
Molecular wt. Range
Mean M i
xi
x M i i
8,000–20,000
14,000
0.05
700
20,000–32,000
26,000
0.15
3900
32,000–44,000
38,000
0.21
7980
44,000–56,000
50,000
0.28
14,000
56,000–68,000
62,000
0.18
11,160
68,000–80,000
74,000
0.10
7400
80,000–92,000
86,000
0.03
2580
M n =
∑ x M = 47,720 g/mol i
i
For PMMA, from Table 14.3, each repeat unit has five carbons, eight hydrogens, and two oxygens. Thus, m = 5( AC) + 8( AH) + 2( AO)
= (5)(12.01 g/mol) + (8)(1.008 g/mol) + (2)(16.00 g/mol) = 100.11 g/mol
Now, we will compute the degree of polymerization using Equation 14.6 as Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
DP =
M n m
=
47,720 g/mol 100.11 g/mol
= 477
Thus, such a homopolymer is not possible since the calculated degree of polymerization is 477 (and not 530).
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.8
High-density polyethylene may be chlorinated by inducing the random substitution of chlorine atoms for hydrogen. (a) Determine the concentration of Cl (in wt%) that must be added if this substitution occurs for 8% of all the original hydrogen atoms. (b) In what ways does this chlorinated polyethylene differ from poly(vinyl chloride)? Solution
(a) For chlorinated polyethylene, we are asked to determine the weight percent of chlorine added for 8% Cl substitution of all original hydrogen atoms. Consider 50 carbon atoms; there are 100 possible side-bonding sites. Ninety-five are occupied by hydrogen and five are occupied by Cl. Thus, the mass of these 50 carbon atoms, mC, is just
mC = 50( AC) = (50)(12.01 g/mol) = 600.5 g
Likewise, for hydrogen and chlorine,
mH = 92( AH) = (92)(1.008 g/mol) = 92.73 g
mCl = 8( ACl) = (8)(35.45 g/mol) = 283.6 g
Thus, the concentration of chlorine, C Cl, is determined using a modified form of Equation 4.3 as
C Cl =
=
mCl mC + mH + mCl
283.6g 600.5 g + 92.73 g + 283.6 g
× 100
× 100 = 29.0 wt%
(b) Chlorinated polyethylene differs from poly(vinyl chloride), in that, for PVC, (1) 25% of the side bonding sites are substituted with Cl, and (2) the substitution is probably much less random.
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Molecular Shape
14.9
For a linear freely rotating polymer molecule, the total extended chain length L depends on the bond length between chain atoms d , the total number of bonds in the molecule N , and the angle between adjacent backbone chain atoms θ , as follows: ⎛ θ ⎞ L = Nd sin ⎜ ⎟ ⎝ 2⎠
(14.11)
Furthermore, the average end-to-end distance r for a randomly winding polymer molecule in Figure 14.6 is equal to
r = d
N
(14.12)
A linear polytetrafluoroethylene has a number-average molecular weight of 500,000 g/mol; compute average values of L and r for this material. Solution This problem first of all asks for us to calculate, using Equation 14.11, the average total chain length, L, for a linear polytetrafluoroethylene polymer having a number-average molecular weight of 500,000 g/mol.
It is necessary to calculate the degree of polymerization, DP , using Equation 14.6.
For polytetrafluoroethylene, from Table 14.3, each repeat unit has two carbons and four flourines. Thus,
m = 2( AC) + 4( AF)
= (2)(12.01 g/mol) + (4)(19.00 g/mol) = 100.02 g/mol
and DP =
M n m
=
500,000 g/mol 100.02 g/mol
= 5000
which is the number of repeat units along an average chain. Since there are two carbon atoms per repeat unit, there are two C—C chain bonds per repeat unit, which means that the total number of chain bonds in the molecule, N , is just (2)(5000) = 10,000 bonds. Furthermore, assume that for single carbon-carbon bonds, d = 0.154 nm and θ = 109° (Section 14.4); therefore, from Equation 14.11
⎛ θ ⎞ L = Nd sin ⎜ ⎟ ⎝ 2⎠
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
⎛ 109° ⎞ ⎟⎥ = 1254 nm ⎝ 2 ⎠⎦
= (10,000)(0.154 nm) ⎢sin ⎜
⎣
It is now possible to calculate the average chain end-to-end distance, r , using Equation 14.12 as
r = d
N = (0.154 nm) 10,000 = 15.4 nm
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.10 Using the definitions for total chain molecule length L (Equation 14.11) and average chain endto-end distance r (Equation 14.12), for a linear polyethylene determine the following: (a) the number-average molecular weight for L = 2,600 nm; (b) the number-average molecular weight for r = 30 nm. Solution (a) This portion of the problem asks for us to calculate the number-average molecular weight for a linear polyethylene for which L in Equation 14.11 is 2,600 nm. It is first necessary to compute the value of N using this equation, where, for the C—C chain bond, d = 0.154 nm, and θ = 109°. Thus
N =
=
L
⎛ θ ⎞ d sin ⎜ ⎟ ⎝ 2⎠
2,600 nm
⎛ 109° ⎞ (0.154 nm) sin ⎜ ⎝ 2 ⎟⎠
= 20,738
Since there are two C—C bonds per polyethylene repeat unit, there is an average of N /2 or 20,738/2 = 10,369 repeat units per chain, which is also the degree of polymerization, DP . In order to compute the value of
n
using Equation 14.6, we must first determine m for polyethylene. Each polyethylene
repeat unit consists of two carbon and four hydrogen atoms, thus
m = 2( AC) + 4( AH)
= (2)(12.01 g/mol) + (4)(1.008 g/mol) = 28.05 g/mol Therefore M n = ( DP)m = (10,369)(28.05 g/mol) = 290,850 g/mol
(b) Next, we are to determine the number-average molecular weight for r = 30 nm. Solving for N from Equation 14.12 leads to N =
r 2 d 2
=
(30 nm) 2 (0.154 nm) 2
= 37,950
which is the total number of bonds per average molecule. Since there are two C—C bonds per repeat unit, then DP = N /2 = 37,950/2 = 18,975. Now, from Equation 14.6
M n = (DP) m = (18,975)(28.05 g/mol) = 532,249 g/mol
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Molecular Configurations
14.11 Sketch portions of a linear polystyrene molecule that are (a) syndiotactic, (b) atactic, and (c) isotactic. Use two-dimensional schematics per footnote 8 of this chapter. Solution We are asked to sketch portions of a linear polystyrene molecule for different configurations (using two-dimensional schematic sketches). (a) Syndiotactic polystyrene
(b) Atactic polystyrene
(c) Isotactic polystyrene
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.12 Sketch cis and trans structures for (a) butadiene, and (b) chloroprene. Use two-dimensional schematics per footnote 11 of this chapter. Solution This problem asks for us to sketch cis and trans structures for butadiene and chloroprene. (a) The structure for cis polybutadiene (Table 14.5) is
The structure of trans butadiene is
(b) The structure of cis chloroprene (Table 14.5) is
The structure of trans chloroprene is
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Thermoplastic and Thermosetting Polymers
14.13 Make comparisons of thermoplastic and thermosetting polymers (a) on the basis of mechanical characteristics upon heating, and (b) according to possible molecular structures. Solution (a) Thermoplastic polymers soften when heated and harden when cooled, whereas thermosetting polymers, harden upon heating, while further heating will not lead to softening. (b) Thermoplastic polymers have linear and branched structures, while for thermosetting polymers, the structures will normally be network or crosslinked.
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.14 (a) Is it possible to grind up and reuse phenol-formaldehyde? Why or why not? (b) Is it possible to grind up and reuse polypropylene? Why or why not? Solution (a) It is not possible to grind up and reuse phenol-formaldehyde because it is a network thermoset polymer and, therefore, is not amenable to remolding. (b) Yes, it is possible to grind up and reuse polypropylene since it is a thermoplastic polymer, will soften when reheated, and, thus, may be remolded.
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Copolymers
14.15 Sketch the repeat structure for each of the following alternating copolymers: (a) poly(butadienechloroprene), (b) poly(styrene-methyl methacrylate), and (c) p oly(acrylonitrile-vinyl chloride). Solution This problem asks for sketches of the repeat unit structures for several alternating copolymers. (a) For poly(butadiene-chloroprene)
(b) For poly(styrene-methyl methacrylate)
(c) For poly(acrylonitrile-vinyl chloride)
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.16 The number-average molecular weight of a poly(styrene-butadiene) alternating copolymer is 1,350,000 g/mol; determine the average number of styrene and butadiene repeat units per molecule. Solution Since it is an alternating copolymer, the number of both types of repeat units will be the same. Therefore, consider them as a single repeat unit, and determine the number-average degree of polymerization. For the styrene repeat unit, there are eight carbon atoms and eight hydrogen atoms, while the butadiene repeat consists of four carbon atoms and six hydrogen atoms. Therefore, the styrene-butadiene combined repeat unit weight is just
m = 12( AC) + 14( AH)
= (12)(12.01 g/mol) + (14)(1.008 g/mol) = 158.23 g/mol
From Equation 14.6, the degree of polymerization is just
DP =
M n m
=
1,350,000 g/mol 158.23 g/mol
= 8,530
Thus, there is an average of 8,530 of both repeat unit types per molecule.
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.17 Calculate the number-average molecular weight of a random nitrile rubber [poly(acrylonitrile butadiene) copolymer] in which the fraction of butadiene repeat units is 0.30; assume that this concentration corresponds to a degree of polymerization of 2500. Solution This problem asks for us to calculate the number-average molecular weight of a random nitrile rubber copolymer. For the acrylonitrile repeat unit there are three carbon, one nitrogen, and three hydrogen atoms. Thus, its repeat unit molecular weight is
mAc = 3( AC) + ( A N) + 3( AH)
= (3)(12.01 g/mol) + 14.01 g/mol + (3)(1.008 g/mol) = 53.06 g/mol
The butadiene repeat unit is composed of four carbon and six hydrogen atoms. Thus, its repeat unit molecular weight is
mBu = 4( AC) + 6( AH)
= (4)(12.01 g/mol) + (6)(1.008 g/mol) = 54.09 g/mol
From Equation 14.7, the average repeat unit molecular weight is just
m = f Ac mAc + f Bu mBu
= (0.70)(53.06 g/mol) + (0.30)(54.09 g/mol) = 53.37 g/mol
Since DP = 2500 (as stated in the problem),
n
may be computed using Equation 14.6 as
Mn = m( DP ) = (53.37 g/mol)(2500) = 133,425 g/mol
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.18 An alternating copolymer is known to have a number-average molecular weight of 250,000 g/mol and a degree of polymerization of 3500. If one of the repeat units is styrene, which of ethylene, propylene, tetrafluoroethylene, and vinyl chloride is the other repeat unit? Why? Solution For an alternating copolymer which has a n umber-average molecular weight of 250,000 g/mol and a degree of polymerization of 3500, we are to determine one of the repeat unit types if the other is styrene. It is first necessary to calculate m using Equation 14.6 as m=
M n DP
=
250,000g/mol 3500
= 71.43g/mol
Since this is an alternating copolymer we know that chain fraction of each repeat unit type is 0.5; that is f s = f x = 0.5, f s and f x being, respectively, the chain fractions of the styrene and unknown repeat units. Also, the repeat unit molecular weight for styrene is
m s = 8( AC) + 8( AH)
= 8(12.01 g/mol) + 8(1.008 g/mol) = 104.14 g/mol
Now, using Equation 14.7, it is possible to calculate the repeat unit weight of the unknown repeat unit type, m x. Thus m x =
=
m − f s m s f x
71.43g/mol − (0.5)(104.14g/mol) 0.5
= 38.72g/mol
Finally, it is necessary to calculate the repeat unit molecular weights for each of the possible other repeat unit types. These are calculated below:
methylene = 2( AC) + 4( AH) = 2(12.01 g/mol) + 4(1.008 g/mol) = 28.05 g/mol m propylene = 3( AC) + 6( AH) = 3(12.01 g/mol) + 6(1.008 g/mol) = 42.0 8 g/mol mTFE = 2( AC) + 4( AF) = 2(12.01 g/mol) + 4(19.00 g/mol) = 100. 02 g/mol mVC = 2( AC) + 3( AH) + ( ACl) = 2(12.01 g/mol) + 3(1.008 g/mol) + 35.45 g/mol = 62.49 g/mol
Therefore, propylene is the other repeat unit type since its m value is almost the same as the calculated m x.
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.19 (a) Determine the ratio of butadiene to styrene repeat units in a copolymer having a numberaverage molecular weight of 350,000 g/mol and degree of polymerization of 4500. (b) Which type(s) of copolymer(s) will this copolymer be, considering the following possibilities: random, alternating, graft, and block? Why? Solution (a) This portion of the problem asks us to determine the ratio of butadiene to styrene repeat units in a copolymer having a weight-average molecular weight of 350,000 g/mol and a degree of polymerization of 4500. It first becomes necessary to calculate the average repeat unit molecular weight of the copolymer, m , using Equation 14.6 as
m=
M n DP
=
350,000g/mol 4500
= 77.78g/mol
If we designate f b as the chain fraction of butadiene repeat units, since the copolymer consists of only two repeat unit types, the chain fraction of styrene repeat units f s is just 1 – f b. Now, Equation 14.7 for this copolymer may be written in the form m = f b mb + f s m s = f b mb + (1 − f b )m s
in which mb and m s are the repeat unit molecular weights for butadiene and styrene, respectively. These values are calculated as follows:
mb = 4( AC) + 6( AH) = 4(12.01 g/mol) + 6(1.008 g/mol) = 54.09 g/mol
m s = 8( AC) + 8( AH) = 8(12.01 g/mol) + 8(1.008 g/mol) = 104.14 g/mol
Solving for f b in the above expression yields
f b =
m − m s mb − ms
=
77.78g/mol − 104.14g/mol 54.09g/mol − 104.14g/mol
= 0.53
Furthermore, f s = 1 – f b = 1 – 0.53 = 0.47; or the ratio is just f b f s
=
0.53 0.47
= 1.1
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
(b) Of the possible copolymers, the only one for which there is a restriction on the ratio of repeat unit types is alternating; the ratio must be 1:1. Therefore, on the basis of the result in part (a), the possibilities for this are random, graft and block.
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.20 Crosslinked copolymers consisting of 60 wt% ethylene and 40 wt% propylene may have elastic properties similar to those for natural rubber. For a copolymer of this composition, determine the fraction of both repeat unit types. Solution For a copolymer consisting of 60 wt% ethylene and 40 wt% propylene, we are asked to determine the fraction of both repeat unit types. In 100 g of this material, there are 60 g of ethylene and 40 g of propylene. The ethylene (C2H4) molecular weight is
m(ethylene) = 2( AC) + 4( AH)
= (2)(12.01 g/mol) + (4)(1.008 g/mol) = 28.05 g/mol
The propylene (C3H6) molecular weight is
m(propylene) = 3( AC) + 6( AH)
= (3)(12.01 g/mol) + (6)(1.008 g/mol) = 42.08 g/mol
Therefore, in 100 g of this material, there are 60 g 28.05 g/mol
= 2.14 mol of ethylene
and 40 g 42.08 g/mol
= 0.95 mol of propylene
Thus, the fraction of the ethylene repeat unit, f (ethylene), is just
f (ethylene) =
2.14 mol 2.14 mol + 0.95 mol
= 0.69
Likewise,
f (propylene) =
0.95 mol 2.14 mol + 0.95 mol
= 0.31
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.21 A random poly(isobutylene-isoprene) copolymer has a number-average molecular weight of 200,000 g/mol and a degree of polymerization of 3000. Compute the fraction of isobutylene and isoprene repeat units in this copolymer. Solution For a random poly(isobutylene-isoprene) copolymer in which
n
= 200,000 g/mol and
DP = 3000, we are asked to compute the fractions of isobutylene and isoprene repeat units. From Table 14.5, the isobutylene repeat unit has four carbon and eight hydrogen atoms. Thus,
mib = (4)(12.01 g/mol) + (8)(1.008 g/mol) = 56.10 g/mol
Also, from Table 14.5, the isoprene repeat unit has five carbon and eight hydrogen atoms, and
mip = (5)(12.01 g/mol) + (8)(1.008 g/mol) = 68.11 g/mol
From Equation 14.7
m = f ib mib + f ip mip
Now, let x = f ib, such that m = 56.10 x + (68.11)(1 − x)
since f ib + f ip = 1. Also, from Equation 14.6
DP =
n
m
Or
3000 =
200,000 g/mol [56.10 x + 68.11(1 − x)] g/mol
Solving for x leads to x = f ib = f (isobutylene) = 0.12. Also,
f (isoprene) = 1 – x = 1 – 0.12 = 0.88
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Polymer Crystallinity
14.22 Explain briefly why the tendency of a polymer to crystallize decreases with increasing molecular weight. Solution The tendency of a polymer to crystallize decreases with increasing molecular weight because as the chains become longer it is more difficult for all regions along adjacent chains to align so as to produce the ordered atomic array.
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.23 For each of the following pairs of polymers, do the following: (1) state whether it is possible to determine whether one polymer is more likely to crystallize than the other; (2) if it is possible, note which is the more likely and then cite reason(s) for your choice; and (3) if it is not possible to decide, then state why. (a) Linear and syndiotactic poly(vinyl chloride); linear and isotactic polystyrene. (b) Network phenol-formaldehyde; linear and heavily crosslinked cis-isoprene. (c) Linear polyethylene; lightly branched isotactic polypropylene. (d) Alternating poly(styrene-ethylene) copolymer; random poly(vinyl chloridetetrafluoroethylene) copolymer. Solution (a) Yes, for these two polymers it is possible to decide.
The linear and syndiotactic poly(vinyl
chloride) is more likely to crystallize; the phenyl side-group for polystyrene is bulkier than the Cl sidegroup for poly(vinyl chloride). Syndiotactic and isotactic isomers are equally likely to crystallize. (b) No, it is not possible to decide for these two polymers. Both heavily crosslinked and network polymers are not likely to crystallize. (c) Yes, it is possible to decide for these two polymers. The linear polyethylene is more likely to crystallize. The repeat unit structure for polypropylene is chemically more complicated than is the repeat unit structure for polyethylene. Furthermore, branched structures are less likely to crystallize than are linear structures. (d) Yes, it is possible to decide for these two copolymers. The alternating poly(styrene-ethylene) copolymer is more likely to crystallize. Alternating copolymers crystallize more easily than do random copolymers.
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3
14.24 The density of totally crystalline polypropylene at room temperature is 0.946 g/cm . Also, at room temperature the unit cell for this material is monoclinic with lattice parameters a = 0.666 nm
α = 90°
b = 2.078 nm
β = 99.62°
c = 0.650 nm
γ = 90°
If the volume of a monoclinic unit cell, V mono, is a function of these lattice parameters as V mono = abc sin β determine the number of repeat units per unit cell. Solution For this problem we are given the density of polypropylene (0.946 g/cm3), an expression for the volume of its unit cell, and the lattice parameters, and are asked to determine the number of repeat units per unit cell. This computation necessitates the use of Equation 3.5, in which we solve forn. Before this can be carried out we must first calculate V C, the unit cell volume, and A the repeat unit molecular weight. For V C
V C = abc sin β
= (0.666 nm)(2.078 nm)(0.650 nm) sin (99.62°)
= 0.8869 nm = 8.869 × 10− cm 3
22
3
The repeat unit for polypropylene is shown in Table 14.3, from which the value of A may be determined as follows:
A = 3( AC) + 6( AH)
= 3(12.01 g/mol) + 6(1.008 g/mol)
= 42.08 g/mol
Finally, solving for n from Equation 3.5 leads to
n =
ρ VC N A A
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
=
(0.946 g/cm 3 )(8.869 ×
10 −22 cm 3 /unit cell )(6.022 × 10 23 repeat units/mol ) 42.08 g/mol
= 12.0 repeat unit/unit cell
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.25 The density and associated percent crystallinity for two polytetrafluoroethylene materials are as follows: 3
ρ (g/cm )
crystallinity (%)
2.144
51.3
2.215
74.2
(a) Compute the densities of totally crystalline and totally amorphous polytetrafluoroethylene. (b) Determine the percent crystallinity of a specimen having a density of 2.26 g/cm3. Solution (a) We are asked to compute the densities of totally crystalline and totally amorphous % crystallinity polytetrafluoroethylene (ρ c and ρ a from Equation 14.8). From Equation 14.8 let C = , 100 such that
C =
ρc (ρ s − ρ a ) ρ s (ρc − ρ a )
Rearrangement of this expression leads to ρc (C ρ s − ρ s ) + ρ c ρ a − C ρ s ρ a = 0
in which ρ c and ρ a are the variables for which solutions are to be found. Since two values of ρ s and C are specified in the problem statement, two equations may be constructed as follows: ρc (C1 ρ s1 − ρ s1 ) + ρ c ρ a − C 1 ρ s1 ρ a = 0 ρc (C2 ρ s 2 − ρ s 2 ) + ρ c ρ a − C 2 ρ s 2 ρ a = 0
In which ρ s1 = 2.144 g/cm3, ρ s2 = 2.215 g/cm3, C 1 = 0.513, and C 2 = 0.742. Solving the above two equations for ρ a and ρ c leads to
ρ a =
=
ρ s1 ρ s 2 (C1 − C 2 ) C1 ρ s1 − C 2 ρ s 2
( 2.144 g/cm 3)( 2.215 g/cm 3) (0.513 − 0.742) = 2.000 g/cm 3 3 3 (0.513) (2.144 g/cm ) − (0.742) ( 2.215 g/cm )
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
And
ρ c =
ρ s1 ρ s 2 (C2 − C 1 ) ρ s 2 (C2 − 1) − ρ s1 (C 1 − 1)
(2.144 g/cm3 )( 2.215 g/cm3 )( 0.742 − 0.513) 3 = = 2.301 g/cm (2.215 g/cm3 )(0.742 − 1) − ( 2.144 g/cm3 )( 0.513 − 1) (b) Now we are to determine the % crystallinity for ρ s = 2.26 g/cm3. Again, using Equation 14.8
% crystallinity =
=
ρc (ρs − ρ a ) ρ s (ρc − ρ a )
× 100
(2.301 g/cm3)( 2.260 g/cm3 − 2.000 g/cm3) × 100 (2.260 g/cm3)( 2.301 g/cm3 − 2.000 g/cm3) = 87.9%
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.26 The density and associated percent crystallinity for two nylon 6,6 materials are as follows: 3
ρ (g/cm )
crystallinity (%)
1.188
67.3
1.152
43.7
(a) Compute the densities of totally crystalline and totally amorphous nylon 6,6. (b) Determine the density of a specimen having 55.4% crystallinity. Solution (a) We are asked to compute the densities of totally crystalline and totally amorphous nylon 6,6 ρ (c and ρ a from Equation 14.8). From Equation 14.8 let C =
C =
% crystallinity 100
, such that
ρc (ρ s − ρ a ) ρ s (ρc − ρ a )
Rearrangement of this expression leads to ρc (C ρ s − ρ s ) + ρ c ρ a − C ρ sρ a = 0
in which ρ c and ρ a are the variables for which solutions are to be found. Since two values of ρ s and C are specified in the problem, two equations may be constructed as follows: ρc (C1 ρ s1 − ρ s1 ) + ρ c ρ a − C 1ρ s1ρ a = 0 ρc (C2 ρ s 2 − ρ s 2 ) + ρ c ρ a − C 2 ρ s 2 ρ a = 0
In which ρ s1 = 1.188 g/cm3, ρ s2 = 1.152 g/cm3, C 1 = 0.673, and C 2 = 0.437. Solving the above two equations for ρ a and ρ c leads to
ρ a =
=
(1.188
ρ s1 ρ s 2 (C1 − C 2 ) C1 ρ s1 − C 2 ρ s 2
g/cm3)(1.152 g/cm3 ) ( 0.673 − 0.437)
(0.673) (1.188
g/cm3
) − (0.437) (1.152
g/cm3
)
= 1.091 g/cm3
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
And
ρ c =
=
(1.188 (1.152
ρ s1 ρ s 2 (C2 − C 1 ) ρ s 2 (C2 − 1) − ρ s1 (C 1 − 1)
g/cm3)(1.152 g/cm3 ) ( 0.437 − 0.673)
g/cm3) ( 0.437 − 1) − (1.188 g/cm3) (0.673 − 1)
= 1.242 g/cm3
(b) Now we are asked to determine the density of a specimen having 55.4% crystallinity. Solving for ρ s from Equation 14.8 and substitution for ρ a and ρ c which were computed in part (a) yields
ρ s =
=
− ρc ρ a C ( ρc − ρa ) − ρ c
− (1.242 g/cm3)(1.091 g/cm3) (0.554) (1.242 g/cm3 − 1.091 g/cm3) − 1.242 g/cm3 3
= 1.170 g/cm
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Diffusion in Polymeric Materials
14.27 Consider the diffusion of water vapor through a polypropylene (PP) sheet 2 mm thick. The pressures of H2O at the two faces are 1 kPa and 10 kPa, which are maintained constant. Assuming conditions of steady state, what is the diffusion flux [in (cm3 STP) / cm2 ⋅ s ] at 298 K? Solution This is a permeability problem in which we are asked to compute the diffusion flux of water vapor through a 2-mm thick sheet of polypropylene. In order to solve this problem it is necessary to employ Equation 14.9. The permeability coefficient of H2O through PP is given in Table 14.6 as 38 × 10−13 (cm3 STP) cm / cm 2 ⋅ s ⋅Pa. Thus, from Equation 14.9
J = P M
P − P ∆ P = P M 2 1 ∆ x ∆x
and taking P 1 = 1 kPa (1,000 Pa) and P 2 = 10 kPa (10,000 Pa) we get 3 ⎡ −13 (cm STP)(cm) ⎤ ⎛ 10,000 Pa − 1,000 Pa ⎞ = ⎢38 × 10 ⎥ ⎜ ⎟⎠ cm 2 ⋅ s ⋅ Pa ⎦ ⎝ 0.2 cm ⎣
= 1.71 × 10−7
3
(cm STP) cm2 ⋅ s
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.28 Argon diffuses through a high density polyethylene (HDPE) sheet 40 mm thick at a rate of 4.0 × 10 (cm STP) / cm2 ⋅ s at 330 K. The pressures of argon at the two faces are 7 000 kPa, and –7
3
2000 kPa, which are maintained constant. Assuming conditions of steady state, what is the permeability coefficient at 330 K? Solution This problem asks us to compute the permeability coefficient for argon through high density polyethylene at 330 K given a steady-state permeability situation. It is necessary for us to use Equation 14.9 in order to solve this problem. Rearranging this expression and solving for the permeability coefficient gives
P M =
J ∆x
∆ P
=
J ∆x P2 − P 1
Taking P 1 = 2000 kPa (2,000,000 Pa) and P 2 = 7000 kPa (7,000,000 Pa), the permeability coefficient of Ar through HDPE is equal to 3 ⎡ −7 (cm STP) ⎤ ⎢ 4.0 × 10 ⎥ (4 cm) 2 cm ⋅ s ⎦ ⎣ P M = (7,000,000Pa − 2,000,000Pa)
= 3.2 × 10
−13
(cm3 STP)(cm) cm ⋅ s ⋅ Pa 2
Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.