AISI 1020 Steel, Cold Rolled

AISI 1020 Steel, cold rolled Categories: Metal; Ferrous Metal; Carbon Steel; AISI 1000 Series Steel; Low Carbon Steel Material Notes:

1020 steel responds well to cold work and heat treating. Weldability is fair. Applications: Shafts, lightly stressed gears, hard wearing surfaces, pins, chains and case hardened parts where core strength is not critical. 1020 is suitable for case hardened parts where core strength is not critical.

Key Words:

UNS G10200, AMS 5032, AMS 5045, ASTM A29, ASTM A108, ASTM A510, ASTM A519, ASTM A29, A108, A510, A512, A513, A519, A544, A575 M10120, A576, A635, A659, A827, A830, BS 970 040A20, 050A20 (En2C), 050A20 (En2D), 060A20, BS 970 Part 1 070M20, DEF STAN95­1­1 C1020, SAE J412, SAE J414, DIN 1.0402, AFNOR CC 20, UNI C 20, SS14 1450 (Sweden), SAE J403

Vendors:

No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.

  Physical Properties Density    Mechanical Properties Hardness, Brinell  Hardness, Knoop  Hardness, Rockwell B  Hardness, Vickers  Tensile Strength, Ultimate  Tensile Strength, Yield  Elongation at Break  Reduction of Area  Modulus of Elasticity  Bulk Modulus 

Metric 7.87 g/cc

English 0.284 lb/in³

Comments

Metric

English

Comments

121 140 68 126 420 MPa

121 140 68 126 60900 psi

Converted from Brinell hardness. Converted from Brinell hardness. Converted from Brinell hardness.

350 MPa 15 % 40 % 186 GPa 148 GPa

50800 psi 15 % 40 % 27000 ksi 21500 ksi

Poissons Ratio  Machinability 

0.29 65 %

0.29 65 %

Shear Modulus 

72.0 GPa

10400 ksi

Metric 0.0000159 ohm­cm

English 0.0000159 ohm­cm

@Temperature 0.000 °C

@Temperature 32.0 °F

0.0000219 ohm­cm

0.0000219 ohm­cm

@Temperature 100 °C

@Temperature 212 °F

0.0000292 ohm­cm

0.0000292 ohm­cm

@Temperature 200 °C

@Temperature 392 °F

Metric 11.7 µm/m­°C

English 6.50 µin/in­°F

  Electrical Properties Electrical Resistivity          Thermal Properties CTE, linear 

 

 

In 50 mm

calculated from elastic modulus and Poisson's ratio Based on AISI 1212 steel. as 100% machinability calculated from elastic modulus and Poisson's ratio Comments condition unknown condition unknown condition unknown Comments

@Temperature 0.000 ­ 100 °C @Temperature 32.0 ­ 212 °F

12.8 µm/m­°C

7.11 µin/in­°F

@Temperature 0.000 ­ 300 °C @Temperature 32.0 ­ 572 °F

 

13.9 µm/m­°C

7.72 µin/in­°F

@Temperature 0.000 ­ 500 °C @Temperature 32.0 ­ 932 °F

Specific Heat Capacity  

0.486 J/g­°C

0.116 BTU/lb­°F

@Temperature >=100 °C

@Temperature >=212 °F

condition unknown

 

0.519 J/g­°C

0.124 BTU/lb­°F

@Temperature 150 ­ 200 °C @Temperature 302 ­ 392 °F

 

0.599 J/g­°C

0.143 BTU/lb­°F

@Temperature 350 ­ 400 °C @Temperature 662 ­ 752 °F

Thermal Conductivity    Component Elements Properties Carbon, C  Iron, Fe  Manganese, Mn  Phosphorous, P  Sulfur, S 

51.9 W/m­K

360 BTU­in/hr­ft²­°F

Typical steel

Metric

English

Comments

0.17 ­ 0.23 % 99.08 ­ 99.53 % 0.30 ­ 0.60 % <= 0.040 % <= 0.050 %

0.17 ­ 0.23 % 99.08 ­ 99.53 % 0.30 ­ 0.60 % <= 0.040 % <= 0.050 %

As remainder

References for this datasheet. Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.