Engineering Standard SAES-L-136 Pipe, Flange and Fitting Material Requirements
9 March 2013
Document Responsibility: Materials and Corrosion Control Standards Committee
Saudi Aramco DeskTop Standards Table of Contents 1
Scope............................................................. 2
2
Conflicts and Deviations................................. 2
3
References..................................................... 2
4
Definitions....................................................... 4
5
General........................................................... 4
6
Requirements by Materials…......................... 5
Previous Issue: 19 December 2011 Next Planned Update: 19 December 2016 Revised paragraphs are indicated in the right margin Primary contact: Anezi, Mohammed Ali on +966-3-8809528 Copyright©Saudi Aramco 2013. All rights reserved.
Page 1 of 8
Document Responsibility: Materials and Corrosion Control Standards Committee SAES-L-136 Issue Date: 9 March 2013 Next Planned Update: 19 December 2016 Pipe, Flange and Fitting Material Requirements
1
Scope This Standard provides requirements for the selection of metallic and non-metallic pipe, flanges and fittings for in-plant and pipeline applications, excluding utility and plumbing piping as defined in SAES-S-060 and SAES-S-070.
2
3
Conflicts and Deviations 2.1
Any conflicts between this standard and other applicable Saudi Aramco Engineering Standards (SAESs), Materials System Specifications (SAMSSs), Standard Drawings (SASDs), or industry standards, codes, and forms shall be resolved in writing by the Company or Buyer Representative through the Manager, Consulting Services Department of Saudi Aramco, Dhahran.
2.2
Direct all requests to deviate from this standard in writing to the Company or Buyer Representative, who shall follow internal company procedure SAEP-302 and forward such requests to the Manager, Consulting Services Department of Saudi Aramco, Dhahran.
References The selection of material and equipment, and the design, construction, maintenance, and repair of equipment and facilities covered by this standard shall comply with the latest edition of these documents to the extent specified in this standard. 3.1
Saudi Aramco References Saudi Aramco Engineering Procedure SAEP-302
Instructions for Obtaining a Waiver of a Mandatory Saudi Aramco Engineering Requirement
Saudi Aramco Engineering Standards SAES-B-064
Onshore and Nearshore Pipeline Safety
SAES-L-100
Applicable Codes and Standards for Pressure Piping Systems
SAES-L-105
Piping Material Specifications
SAES-L-131
Fracture Control of Line Pipe
SAES-L-133
Corrosion Protection Requirements for Pipelines/Piping
SAES-L-310
Design of Plant Piping Page 2 of 8
Document Responsibility: Materials and Corrosion Control Standards Committee SAES-L-136 Issue Date: 9 March 2013 Next Planned Update: 19 December 2016 Pipe, Flange and Fitting Material Requirements
SAES-L-410
Design of Pipelines
SAES-L-620
Design of Nonmetallic Piping in Hydrocarbon and Water Injection Systems
SAES-L-650
Construction of Nonmetallic Piping in Hydrocarbon and Water Injection Systems
SAES-S-060
Saudi Aramco Plumbing Code
SAES-S-070
Installation of Utility Piping Systems
SAES-W-011
Welding Requirements for On-Plot Piping
Saudi Aramco Materials System Specifications
3.2
01-SAMSS-035
API Line Pipe
01-SAMSS-038
Small Direct Charge Purchases of Pipe
01-SAMSS-042
Reinforced Thermoset Resin (RTR) Pipe and Fittings in Water and Hydrocarbon Services
01-SAMSS-043
Carbon Steel Pipes for On-Plot Piping
01-SAMSS-044
CRA Clad Pipe Spools
01-SAMSS-048
CRA Clad or Lined Steel Pipe
01-SAMSS-333
High Frequency Welded Line Pipe
02-SAMSS-005
Butt Welding Pipe Fittings
02-SAMSS-011
Forged Steel and Alloy Flanges
02-SAMSS-012
Weld Overlayed Fittings, Flanges and Spool Pieces
Industry Codes and Standards American Petroleum Institute API SPEC 5L
Specification for Line Pipe
American Society of Mechanical Engineers ASME B31.3
Process Piping
ASME B31.4
Liquid Transportation Systems for Hydrocarbons, LPG, Anhydrous Ammonia, and Alcohols
ASME B31.8
Gas Transmission and Distribution Systems
Page 3 of 8
Document Responsibility: Materials and Corrosion Control Standards Committee SAES-L-136 Issue Date: 9 March 2013 Next Planned Update: 19 December 2016 Pipe, Flange and Fitting Material Requirements
4
Definitions Code: The appropriate code (ASME B31.3, ASME B31.4, or ASME B31.8) as specified in SAES-L-100. Pipe fittings: are elbows, tees, welding outlets, reducers, caps and lap joint stub ends; as well as blind flanges, spectacle plates, spacers and slip blinds. Transportation Pipelines: Pipelines constructed to ASME B31.4 or ASME B31.8 codes. See SAES-L-100.
5
General 5.1
Saudi Aramco Materials System Specifications 5.1.1
Carbon steel pipe for pipelines and on-plot applications shall be in accordance with the applicable specification (SAMSS) as follows: 01-SAMSS-035
API Line Pipe
01-SAMSS-038
Small Direct Charge Purchases of Pipe
01-SAMSS-333
High Frequency Welded Line Pipe
01-SAMSS-043
Carbon Steel Pipes for On-Plot Piping
Commentary: The scope of 01-SAMSS-038 “Small Direct Charge Purchase of Pipes” does not cover ASTM pipes. Hence, small quantity ASTM A106 Grade B pipes, intended for on-plot applications, shall be substituted by API SPEC 5L Grades as allowed by SAES-L-105 to allow procurement of small quantities from stockists in accordance with 01-SAMSS-038.
5.3
5.1.2
Non-Metallic Pipe shall be in accordance with 01-SAMSS-042: Reinforced Thermoset Resin (RTR) Pipe and Fittings in Water and Hydrocarbon Services.
5.1.3
CRA (Corrosion Resistant Alloy) Clad or Lined Pipe shall be in accordance with 01-SAMSS-048: CRA Clad or Lined Steel Pipe.
5.1.4
CRA (Corrosion Resistant Alloy) weld overlayed flanges and fittings shall be procured in accordance with 02-SAMSS-012.
5.15
CRA clad pipe spools shall be procured in accordance with 01-SAMSS-044.
Seamless pipe intended for sour service shall not be procured as sour service pipe in accordance with API SPEC 5L. HIC testing is not required for seamless Page 4 of 8
Document Responsibility: Materials and Corrosion Control Standards Committee SAES-L-136 Issue Date: 9 March 2013 Next Planned Update: 19 December 2016 Pipe, Flange and Fitting Material Requirements
pipes intended for sour service and procured in accordance with 01-SAMSS-035 and 01-SAMSS-043. 5.4
6
HIC test is required for small quantity seamless pipes intended for sour service and procured in accordance with 01-SAMSS-038.
Requirements by Material The following requirements apply in addition to those given in the applicable Code: 6.1
Furnace butt-welded pipe shall not be used.
6.2
Cast iron pipe and fittings may only be used for utility and plumbing services as defined in SAES-S-060 and SAES-S-070.
6.3
Nonmetallic Reinforced Thermoset Resin (RTR) pipe shall be used per 01-SAMSS-042, SAES-L-620 and SAES-L-650. For material service compatibility, nonmetallic specialist of ME&CCD/CSD shall be consulted.
6.4
Carbon steel pipe shall have specified minimum yield strength (SMYS) of not less than 35 ksi (241 MPa) equivalent to ASTM A106 Grade B or higher.
6.5
The highest grade for all types of pipes shall be restricted to API 5L Grade X-65 for sour service and API 5L Grade X-70 for non-sour service.
6.6
Restrictions on use of High Frequency Welded (HFI or ERW) carbon steel pipe. 6.6.1
6.6.2
High Frequency Welded pipe shall comply with the following requirements: a)
For sour gas or corrosive services, as defined in SAES-L-133, high frequency welded pipe manufactured in accordance with Class C requirements of 01-SAMSS-333 shall be used with exceptions listed in 6.6.2.
b)
For all other services not covered in (a) above, pipes manufactured in accordance with Class B requirements of 01-SAMSS-333 shall be used with exceptions listed in 6.6.2.
ERW pipe shall not be used in the following applications: a)
On-plot piping in accordance with ASME B31.3 or ASME B31.1 except for firewater systems.
b)
ASME B31.8 Gas pipelines in sour or corrosive services, as defined in SAES-L-133, in locations Class 3 and Class 4 as defined in SAES-B-064. Page 5 of 8
Document Responsibility: Materials and Corrosion Control Standards Committee SAES-L-136 Issue Date: 9 March 2013 Next Planned Update: 19 December 2016 Pipe, Flange and Fitting Material Requirements
6.7
6.8
c)
ASME B31.8 Gas pipelines within 500 meters of the battery limits of plants and permanently manned facilities.
d)
Grade X70 and above in sour service.
e)
In low temperature service (below 0°C).
f)
For offshore applications.
g)
Backing Carbon Steel Material for Lined or Weld Overlayed Pipes.
Restrictions on use of Spiral Weld Pipe 1.
Spiral weld pipe shall not be used in sour services, either for ASME B31.3 in-plant piping or for ASME B31.4 or ASME B31.8 pipelines.
2.
Spiral welded pipe shall not be used for on-plot piping
3.
Backing Carbon Steel Material for Lined or Weld Overlayed Pipes.
Restrictions on use of mechanically bonded Lined Pipe Mechanically bonded lined pipe shall not be used in subsea applications.
6.9
Longitudinally welded pipe used in ASME B31.3 on-plot piping, shall be in the heat treated, stress relieved condition or cold expanded in the following services. i.
Sour services as defined in SAES-L-133
ii.
All caustic (NaOH) solutions, including conditions where caustic carryover may occur (e.g., downstream from caustic injection points)
iii.
All monoethanolamine (MEA) solutions (all temperatures)
iv.
All diglycol amine (DGA) solutions above 138°C design temperature
v.
All rich amino diisopropanol (ADIP) solutions above 90°C design temperature
vi.
All lean ADIP solutions above 60°C design temperature
vii. Boiler deaerator service (i.e., ambient temperature vacuum deaerators are exempt) viii. All diethanolamine (DEA) solutions ix.
All MDEA / aMDEA solutions Commentary Note: The above provisions are related to reducing the probability of stress corrosion cracking and stress-oriented hydrogen-induced cracking (SOHIC). SAES-L-133 also addresses corrosion and environmental cracking
Page 6 of 8
Document Responsibility: Materials and Corrosion Control Standards Committee SAES-L-136 Issue Date: 9 March 2013 Next Planned Update: 19 December 2016 Pipe, Flange and Fitting Material Requirements considerations.
6.10
Pipe per API SPEC 5L grades X65 and X70 shall be derated to X60 when used for ASME B31.3 on-plot piping API SPEC 5L Grade X70 pipe shall not be used in any sour service even if derated. The pipe shall be marked with the actual grade. In addition, girth weld requirements established in Saudi Aramco welding standard SAES-W-011 for grades X65 or X70 shall be followed. 70 High Frequency (HFI) welded pipes shall not be used for sour service as indicated in paragraph 6.5.2(d) above.
6.11
Low Temperature Piping Requirements 6.11.1 When the design minimum temperature (defined in SAES-L-310 or SAES-L-410 as applicable) is at minus -18°C and above, pipe in accordance with 01-SAMSS-035, 01-SAMSS-038, 01-SAMSS-043 or 01-SAMSS-333 shall be used. 6.11.2 When the minimum design temperature is within the range of -18°C to 45°C inclusive, carbon steel piping and components shall be as specified in this section 6.11.2.1
ERW pipe shall not be used below 0°C design temperature.
6.11.2.2
Pipe purchased in accordance with the specifications listed below may be used if longitudinal Charpy V-notch impact tests at -45°C demonstrate absorbed energies of 34/27 J (25/20 ft-lbs): a)
ASTM A333 Grade 6
b)
ASTM A671, Class 22, Grade CC60 or CC65, Supplementary Requirement S-2 (Charpy V-Notch Test)
6.11.3 ANSI/ASME B16.11 socket-welding and threaded fittings, less than 2-inch NPS, manufactured in accordance with ASTM A350 Grade LF2 Class 1, can be used down to a minimum design temperature of -45°C. 6.11.4 Pipe fittings for low temperature shall comply with the requirements of 02-SAMSS-005. Acceptable materials are ASTM A420 Grade WPL 6, and ASTM A350 Grade LF2 Class 1. ASTM A516 plate maybe used for blind flanges, spectacle plates, spacers and slip blinds. 6.11.5 All weld neck flanges, and any lap joint flanges shall comply with requirements specified in 02-SAMSS-011.
Page 7 of 8
Document Responsibility: Materials and Corrosion Control Standards Committee SAES-L-136 Issue Date: 9 March 2013 Next Planned Update: 19 December 2016 Pipe, Flange and Fitting Material Requirements
6.11.6 Carbon steel pipe for sour service shall comply with 01-SAMSS-035 for pipelines, or 01-SAMSS-043 for on-plot piping. Carbon steel pipe fittings for sour service shall comply with 02-SAMSS-005. Flanges for sour service shall comply with 02-SAMSS-011. 6.12
The additional requirements of 01-SAMSS-035 shall be applied as specified in SAES-L-131 for fracture control of transportation pipelines.
19 December 2011 9 March 2013
Revision Summary Major revision. Editorial revision to clarify prohibiting ERW & Spiral pipes to be used as backing carbon steel material for lined and weld overlayed pipes, which is already stated in 01-SAMSS-048.
Page 8 of 8